PU Plast

Product variant for
General «
General
Automotive

PU PLAST is a two component, room temperature
curing, black coloured, odourless, thixotropic
polyurethane adhesive specially designed for structural bonding of a wide range of materials as thermosetting and thermoplastic materials, steel, aluminium, concrete, wood and glas.

  • Fast curing
  • The drying process starts after 45 seconds
  • Sanding after 15 minutes
  • Room temperature curing
  • Resists: Motor oil, Paraffin, Acetic Acid, Petrol, water , solvents, temperatures up to 90°C
  • High filling  properties
  • Bonds various materials
  • Non-shrinking properties
  • Ideal grinding till zero
Article nr Name Content
T910001 PU Plast black 5 min. 50ml 50ml
T910002 PU Plast clear 1min. 50ml 50ml
T910006 PU Plast black 1 min. 50ml 50ml
T911350 Applicator 50 ml TMT 1:1 / 2:1 / 10:1 1pc.
Y911303 Mixer Tip 50ml blue 10pcs.
Y911600 Reinforcement Tissue 12x360cm 1pc.
Y911601 Contouring Tissue 12x360cm 1pc.

» To the shop
  • Technical data
  • Application and usage
  • Downloads

PU Plast black 1 min. (PART A):
Aggregate State: Liquid
Colour: black
Odour: characteristic
Initial boiling point and boiling range: > 200 °C
Flash point: 182 °C
Vapour pressure: 0.1 Pa
Density: 1 g/cm³
Dynamic viscosity: 3,000 mPa* s

PU Plast black 1 min. (PART B):
Aggregate State: Liquid
Colour: copper
Odour: characteristic
Initial boiling point and boiling range: > 300 °C
Flash point: 205 °C
Vapour pressure: 0.01 Pa
Density: 1.2 g/cm³
Dynamic viscosity: 4,000 mPa* s
Self ignition temperature > 600 °C

PU Plast black 5 min. (PART A):
Aggregate State: Liquid
Colour: black
Odour: characteristic
Initial boiling point and boiling range: > 200 °C
Flash point: 182 °C
Vapour pressure: 0.1 Pa
Density: 1 g/cm³
Dynamic viscosity: 3000 mPa* s

PU Plast black 5 min. (PART B):
Aggregate State: Liquid
Colour: copper
Odour: characteristic
Initial boiling point and boiling range: > 300 °C
Flash point: 205 °C
Vapour pressure: 0.01 Pa
Density: 1.2 g/cm³
Dynamic viscosity: 4,000 mPa* s
Self ignition temperature > 600 °C

  • AUTOMOTIVE:
    For fast bonding of broken plastic and metal parts. Different brackets  on bumpers, covers, plastic  tanks ,  headlamps rear lights and windows mechanism. Trimming and tuning parts, repairs of damaged holes and screws…
  • INDUSTRIES:
    Repair of window and door components made of plastic, wood, metal and aluminum, make install from, plates, letters, reapair in industrial electronics , mechanics, indoor and outdoor maintainance.
  • Preparing and Mixing:
    The parts must be cleaned free of grease and have to be dryed completely
    For better results the parts have to be sanded  before clueing
    Using temperature +5°C to +30°C
    Use the clue only wih the standard mixing nozzles.

PU Plast

Product variant for
 «
General
Automotive

PU Plast is a two component polyurethane-based
adhesive, that cures at room temperature.
Ideal for bonding a wide range of thermoplastic
materials, thermosetting plastics, steel, aluminum,
concrete, wood, glass. The product can be overpainted and excellent results can be obtain if used with plasters for plastic materials as our NOVA BLACK MAGIC.

  • Two component polyurethane-based adhesive
  • It cures at room temperature
  • Bonding of a wide range of thermoplastic materials,  thermosetting plastics, steel, aluminium, concrete, wood and glass.
  • It can be overpainted.
  • Excellent results if used in combination with plasters for plastic materials, for example “NOVA BLACK MAGIC”.  
Article nr Name Content
T910001 PU Plast black 5 min. 50ml 50ml
T910002 PU Plast clear 1min. 50ml 50ml
T910006 PU Plast black 1 min. 50ml 50ml
T911350 Applicator 50 ml TMT 1:1 / 2:1 / 10:1 1pc.
Y911303 Mixer Tip 50ml blue 10pcs.
Y911600 Reinforcement Tissue 12x360cm 1pc.
Y911601 Contouring Tissue 12x360cm 1pc.

» To the shop
  • Technical data
  • Application and usage
  • Downloads

Base : Polyurethane
Volume mixing ratio: 1:1
Weight mixing ratio: 0,89:1
Colour : black/grey
Aspect : Thixotropic
Viscosity: 50.000 mPas
Relative density : 1,12
Temperature resistance  : -37° /+ 100°C
Application temperature : +10°/+30°C.
Flammability : > 200°C.

Water solubility : insoluble
Traction resistance: 22N/mm2
Elongation at break: 15%
Hardness: shore 80D
Resistivity:  1,2x10^12 Ohm xcm

Open time: 5 minutes / 1 minute
Setting time: 15 minutes / 5 minutes
Final catalysis: 8 hours / 4 hours

  • Ideal for repairing plastic accessories, for example bumpers, masks, headlights, door panels, fairings motorcycle, scooter .... 
  • It adheres to the most of the plastic materials except PP,PE,PTFE. In order to improve the adhesion it is possible to use PU PLAST with some specific primers for plastic materials, for example our “Primer 903” and “Fix Primer”.
  • Advice: in order to obtain a good result it is necessary to prepare the surface using medium grit sandpaper to roughening and cleaning it with a cleaner, for example our “MULTIFOAM.

PU Plast

Product variant for
 «
General
Automotive

PU PLAST is a two component, room temperature
curing, black coloured, odourless, thixotropic
polyurethane adhesive specially designed for structural bonding of a wide range of materials as thermosetting and thermoplastic materials, steel, aluminium, concrete, wood and glas.

  • Fast curing
  • The drying process starts after 45 seconds
  • Sanding after 15 minutes
  • Room temperature curing
  • Resists: Motor oil, Paraffin, Acetic Acid, Petrol, water , solvents, temperatures up to 90°C
  • High filling  properties
  • Bonds various materials
  • Non-shrinking properties
  • Ideal grinding till zero
Article nr Name Content
T910001 PU Plast black 5 min. 50ml 50ml
T910002 PU Plast clear 1min. 50ml 50ml
T910006 PU Plast black 1 min. 50ml 50ml
T911350 Applicator 50 ml TMT 1:1 / 2:1 / 10:1 1pc.
Y911303 Mixer Tip 50ml blue 10pcs.
Y911600 Reinforcement Tissue 12x360cm 1pc.
Y911601 Contouring Tissue 12x360cm 1pc.

» To the shop
  • Technical data
  • Application and usage
  • Downloads

PU Plast black 1 min. (PART A):
Aggregate State: Liquid
Colour: black
Odour: characteristic
Initial boiling point and boiling range: > 200 °C
Flash point: 182 °C
Vapour pressure: 0.1 Pa
Density: 1 g/cm³
Dynamic viscosity: 3,000 mPa* s

PU Plast black 1 min. (PART B):
Aggregate State: Liquid
Colour: copper
Odour: characteristic
Initial boiling point and boiling range: > 300 °C
Flash point: 205 °C
Vapour pressure: 0.01 Pa
Density: 1.2 g/cm³
Dynamic viscosity: 4,000 mPa* s
Self ignition temperature > 600 °C

PU Plast black 5 min. (PART A):
Aggregate State: Liquid
Colour: black
Odour: characteristic
Initial boiling point and boiling range: > 200 °C
Flash point: 182 °C
Vapour pressure: 0.1 Pa
Density: 1 g/cm³
Dynamic viscosity: 3000 mPa* s

PU Plast black 5 min. (PART B):
Aggregate State: Liquid
Colour: copper
Odour: characteristic
Initial boiling point and boiling range: > 300 °C
Flash point: 205 °C
Vapour pressure: 0.01 Pa
Density: 1.2 g/cm³
Dynamic viscosity: 4,000 mPa* s
Self ignition temperature > 600 °C

  • AUTOMOTIVE:
    For fast bonding of broken plastic and metal parts. Different brackets  on bumpers, covers, plastic  tanks ,  headlamps rear lights and windows mechanism. Trimming and tuning parts, repairs of damaged holes and screws…
  • INDUSTRIES:
    Repair of window and door components made of plastic, wood, metal and aluminum, make install from, plates, letters, reapair in industrial electronics , mechanics, indoor and outdoor maintainance.
  • Preparing and Mixing:
    The parts must be cleaned free of grease and have to be dryed completely
    For better results the parts have to be sanded  before clueing
    Using temperature +5°C to +30°C
    Use the clue only wih the standard mixing nozzles.