BOND SEAL SUPER is the most high tech adhesive kit with an extremely quick and very powerful setting on the widest range of materials. This solvent and isocyanate-free assembly adhesive has a very high tensile strength and does not show signs of ageing. BOND SEAL SUPER is neutral and acid-free, and can be used on a variety of materials, even natural stone. BOND SEAL SUPER allows for 40 mm adhesive strips without any deformation.
| Article nr | Name | Content |
|---|---|---|
| T534201 | Bond Seal Super white 290ml | 290ml |
Basis: MS-polymer.
Physical state: Paste
Colour: white
Odour: odourless
Application Temperature: + 5° C / + 40° C
Application rate (2,5 mm / 6,3 bar): 20 g/min
Flow (ISO 7390): < 2 mm
Initial boiling point and boiling range: < 34°C
Vapour pressure (at 20°C): 93 Pa
Vapour pressure (at 50°C): 482,44 Pa (0,48 kPa)
Density (at 20°C): 1.658 kg/m³
Relative density (at 20°C): 1,658
Kinematic viscosity (at 40°C): > 20,5 cSt
Solubility properties: Soluble in organic solvents
Flash point: > 180°C
Self ignition temperature: ≈420 ºC
Skin over time (23° C / 50% RH): 15 min.
Curing after 24 hours (23° C / 50% RH): ± 2-3 mm/24 hours.
UV, weather and water resistant: yes
Frost resistant till -15° C during transport: yes
Temperature resistance after curing: - 40° C / + 90° C
Mechanical properties: 2 mm film
Shore-A hardness (3s, DIN 53505): 60
100% Modulus (DIN 53504): 1,39 MPa
Tensile strength (DIN 53504): 2,2 MPa
Elongation at break (DIN 53504): 335 %
VOC content: 2,23-2,34 % (35,6-36,1 g/l)
BOND SEAL SUPER is the most high tech adhesive kit with an extremely quick and very powerful setting on the widest range of materials. This solvent and isocyanate-free assembly adhesive has a very high tensile strength and does not show signs of ageing. BOND SEAL SUPER is neutral and acid-free, and can be used on a variety of materials, even natural stone. BOND SEAL SUPER allows for 40 mm adhesive strips without any deformation.
| Article nr | Name | Content |
|---|---|---|
| T534201 | Bond Seal Super white 290ml | 290ml |
Basis: MS-polymer.
Physical state: Paste
Colour: white
Odour: odourless
Application Temperature: + 5° C / + 40° C
Application rate (2,5 mm / 6,3 bar): 20 g/min
Flow (ISO 7390): < 2 mm
Initial boiling point and boiling range: < 34°C
Vapour pressure (at 20°C): 93 Pa
Vapour pressure (at 50°C): 482,44 Pa (0,48 kPa)
Density (at 20°C): 1.658 kg/m³
Relative density (at 20°C): 1,658
Kinematic viscosity (at 40°C): > 20,5 cSt
Solubility properties: Soluble in organic solvents
Flash point: > 180°C
Self ignition temperature: ≈420 ºC
Skin over time (23° C / 50% RH): 15 min.
Curing after 24 hours (23° C / 50% RH): ± 2-3 mm/24 hours.
UV, weather and water resistant: yes
Frost resistant till -15° C during transport: yes
Temperature resistance after curing: - 40° C / + 90° C
Mechanical properties: 2 mm film
Shore-A hardness (3s, DIN 53505): 60
100% Modulus (DIN 53504): 1,39 MPa
Tensile strength (DIN 53504): 2,2 MPa
Elongation at break (DIN 53504): 335 %
VOC content: 2,23-2,34 % (35,6-36,1 g/l)
We use our own and third-party cookies to personalize content and advertisements, to be able to offer functions for social media and to analyze access to our website. The cookies are described in more detail under "Cookie Settings" and can be activated or deactivated. By clicking on "Allow all cookies" you agree to their use. You can subsequently change your cookie settings on the "Privacy Policy" page. Additional Information: Privacy policy incl. cookie settings | General terms and conditions